  • Thumbnail Image
    ItemOpen Access
    Nitriding behavior of Ni and Ni-based binary alloys
    (2015) Fonovic, Matej; Mittemeijer, Eric J. (Prof. Dr. Ir.)
    Gaseous nitriding is a prominent thermochemical surface treatment process which can improve various properties of metallic materials such as mechanical, tribological and/or corrosion properties. This process is predominantly performed by applying NH3+H2 containing gas atmospheres serving as the nitrogen donating medium at temperatures between 673 K and 873 K (400 °C and 600 °C). NH3 decomposes at the surface of the metallic specimen and nitrogen diffuses into the surface adjacent region of the specimen whereas hydrogen remains in the gas atmosphere. One of the most important parameters characterizing a gaseous nitriding process is the so-called nitriding potential (rN) which determines the chemical potential of nitrogen provided by the gas phase. The nitriding potential is defined as where and are the partial pressures of the NH3 and H2 in the nitriding atmosphere. In contrast with nitriding of alpha-Fe where the nitriding potential is usually in the range between 0.01 and 1 atm-1/2, nitriding of Ni and Ni-based alloys requires employing nitriding potentials higher than 100 atm-1/2 and even up to infinity (nitriding in pure NH3 atmosphere). This behavior is compatible with decreased thermodynamic stability of the 3d-metal nitrides with increasing atomic number. Depending on the nitriding conditions (temperature, nitriding potential and treatment time), different phases are formed at the surface of the Ni-based alloys. By applying very high nitriding potential, formation of hexagonal Ni3N at the surface of the specimen (known as external nitriding) leads to the development of a compound layer, which may improve tribological properties. Underneath the Ni3N compound layer, two possibilities exist: (i) alloying element precipitation within the nitrided zone (known as internal nitriding) and/or (ii) development of metastable and precipitate-free microstructure known as expanded austenite or S-phase, which can enhance surface hardness, fatigue properties and corrosion properties.Nitriding of multicomponent Ni-based alloys is usually applied in the industry. Nevertheless, the understanding of nitriding is mostly based on phenomenological research and experience. Thereby there is still absence of complete understanding of nitriding of Ni-based alloys, which requires further detailed investigations. Since studying the nitrided multicomponent alloys is complicated, in this thesis fundamental investigations were performed on pure nickel and binary Ni-based model alloys.This thesis focuses on the nitriding behavior of pure nickel, which will result with an thermodynamic evaluation of the Ni-N system. Furthermore, deeper insights in the nitriding behavior of the binary Ni-based alloys is obtained upon nitriding Ni-4 wt.% Ti and Ni-2 wt.% Ti (Ni-5 at.% Ti and Ni-2.5 at.% Ti) alloys. Thereby, the development of large residual macrostresses parallel to the surface of the specimen is related with the N concentration gradient in the nitrided zone.
  • Thumbnail Image
    ItemOpen Access
    Ion beam lithographic and multilayer fresnel zone plates for soft and hard X-rays: nanofabrication and characterization
    (2015) Keskinbora, Kahraman; Schütz, Gisela (Prof. Dr.)
    X-ray microscopy has become an important analytical characterization method for a plethora of applications in materials science, physics, chemistry and biology, thanks to the emergence of modern synchrotron radiation facilities. These facilities enable high brilliance, energy tunable, variable polarization X-rays which gives access to mass density, elemental, chemical, electronic and magnetic properties of materials. In the soft X-ray energies nearly all elements can be probed by spectromicroscopic methods. Another important property of synchrotron radiation is the time structure in the ns to ps range, which can be utilized for sophisticated time resolution studies. These opportunities can be combined with high spatial resolution which is determined by the focusing method and the optic. Focusing of X-rays has historically been a difficult task due to strong absorption and weak phase shift of X-rays within matter. The required phase shift of X-rays, which depends on the real part of the complex refractive index, differs from 1 (the vacuum refractive index) only on the order of 10^-2 to 10^-6 and conventional lenses do not work. One very successful X-ray optic is the Fresnel Zone Plate (FZP), a diffractive optic that act as a lens under certain conditions and can focus X-rays to nanometer sized spots. The resolution of the FZP depends on the width of the outermost zone and is highly correlated with the smallest feature that can be fabricated. Conventionally, the e-beam lithography (EBL) is used for production FZPs which could resolve up to 10 nm structures with serious limitations. One difficulty of EBL is its ever increasing complexity for many-step fabrication of smaller features or intricate geometries. Therefore, EBL is mostly constrained to planar, binary geometries with moderate efficiencies strongly decreasing with energy and not effective for hard X-rays. Special 3D geometries in the form of kinoform lenses can theoretically have 100 % focusing efficiencies. Attempts to approximate these geometries via EBL increased the number of process steps even further. The smallest FZP feature size even for low aspect ratios achievable via EBL is fundamentally limited due to the proximity effect which is the interaction and spread of electrons within the resist material. We addressed these issues by focusing our research on alternative FZP fabrication techniques as high-speed ion beam lithography (IBL), and gray scale ion lithography to realize efficient kinoforms. Another approach towards full-material multilayer FZPs with infinite aspect ratio was based on atomic layer deposition (ALD) with subsequent ion beam slicing. Each of these three methods targets specific challenges faced by the e-beam lithography based FZP fabrication techniques. All the fabricated FZPs were tested for their resolution and efficiency performances at a state of the art scanning transmission X-ray microscope at BESSY for soft X-rays and/or at optical test stations at ESRF and PETRA III for hard X-rays. Using IBL the rapid preparation of a 110 nm thick Au FZP with 50 µm diameter and 50 nm ∆r in less than 13 minutes is demonstrated. Employed for X-ray microscopy, the FZP clearly resolved 28.5 nm features with a cut-off of 24.3 nm at ~1120 eV. Additional process improvements were made towards smaller zones with higher zone quality. They allowed the preparation of a FZP with 30 nm outermost half-period remarkably, in about 8 min. This FZP was shown to clearly resolve 21 nm features on a multilayer test object with large room for improvement. This high through-put FZP production route is of special interest not only concerning the low cost and easy availability. A large array of these optical components is attractive, for experiments such as one-shot ultra-high brilliance FEL investigations due to the radiation damage or for instance for coded-aperture arrays for high-angle resolving X-ray astronomy. Towards fabrication of kinoforms for high efficiency X-ray focusing, we have performed various materials optimization studies in order to achieve a high surface quality optic. After various trials the materials were finally optimized and the fabricated lenses achieved more than 14 % absolute diffraction efficiency that is almost 90 % compared to the theoretical prediction. This confirms how closely we were able to replicate the ideal three dimensional surface relief structure for the first time. It was possible to carry out imaging with these lenses with half-pitch resolutions down to 60 nm. The kinoform lenses were tested at the soft X-ray range where a significant absorption is present in materials. These results also potentially pave the way for very high efficiency hard X-ray focusing which can in principle be utilized in laboratory based X-ray sources, X-ray astronomy and the new rising field of X-ray ptychography. To fabricate high resolution ML-FZPs, Al2O3/Ta2O5multilayers, deposited on a smooth glass optical fiber via atomic layer deposition using non-dedicated instruments were carefully cut-out, sliced and polished to a high quality surface finish using focused ion beams. Following the transfer of the slice to a TEM grid as holder the slices were polished to a high surface finish quality, also via a focused ion beam. Fabricated ML-FZPs were synchrotron tested using an in-house constructed 2-axis tilt stage specially designed for aligning ML-FZP with respect to the X-ray optical axis. The results showed that it was possible to resolve 21 nm features in direct imaging at 1200 eV and sub-30 nm focusing at 8 keV. This is the highest demonstrated resolving power for a multilayer type FZP, to date to the best of our knowledge. Results exhibit the potential for high-resolution hard X-ray focusing where this type of optics are especially efficient. For ultra-high resolution hard and soft X-ray imaging, with potentially achievable ∆r of a few nm is well below what can be achieved through any lithography method available today.