Browsing by Author "Al-Ahmad, Ali"

Now showing 1 - 2 of 2

Open Access
Copper-enriched hydroxyapatite coatings obtained by high-velocity suspension flame spraying : effect of various gas parameters on biocompatibility
(2024) Le, Long-Quan R. V.; Lanzino, M. Carolina; Blum, Matthias; Höppel, Anika; Al-Ahmad, Ali; Killinger, Andreas; Gadow, Rainer; Rheinheimer, Wolfgang; Seidenstuecker, Michael
Hydroxyapatite (HAp)-coated bone implants are frequently used for orthopaedic or dental implants since they offer high biocompatibility and osteoconductivity. Yet, problems such as infections, e.g. periprosthetic joint infections, occur when implanting foreign material into the body. In this study, HAp coatings were produced via high-velocity suspension flame spraying (HVSFS). This method allows for the production of thin coatings. We investigated the effects of different gas parameters on the coating properties and on the biocompatibility, which was tested on the human osteosarcoma cell line MG63. Furthermore, Copper (Cu) was added to achieve antibacterial properties which were evaluated against standard microorganisms using the airborne assay. Three gas parameter groups (low, medium, and high) with different Cu additions (0 wt.%, 1 wt.% and 1.5 wt.%) were evaluated. Our findings show that porosity as well as hardness can be controlled through gas parameters. Furthermore, we showed that it is possible to add Cu through external injection. The Cu content in the coating as well as the release varies with different gas parameters. Both antibacterial efficacy as well as biocompatibility are affected by the Cu content. We could significantly reduce the amount of colony-forming units (CFU) in all coatings for E. coli , CFU for S. aureus was reduced by adding 1.5 wt.% of Cu to the coating. The biocompatibility testing showed a cytotoxicity threshold at a Cu-release of 14.3 mg/L in 120 hours. Based on our findings, we suggest medium gas parameters for HVSFS and the addition of 1 wt.% Cu to the coating. With these parameters, a reasonable antibacterial effect can be achieved while maintaining sufficient biocompatibility.
Open Access
Suspension-sprayed calcium phosphate coatings with antibacterial properties
(2024) Lanzino, Maria Carolina; Le, Long-Quan R. V.; Höppel, Anika; Killinger, Andreas; Rheinheimer, Wolfgang; Dembski, Sofia; Al-Ahmad, Ali; Mayr, Hermann O.; Seidenstuecker, Michael
Prosthesis loosening due to lack of osteointegration between an implant and surrounding bone tissue is one of the most common causes of implant failure. Further, bacterial contamination and biofilm formation onto implants represent a serious complication after surgery. The enhancement of osteointegration can be achieved by using bioconductive materials that promote biological responses in the body, stimulating bone growth and thus bonding to tissue. Through the incorporation of antibacterial substances in bioconductive, biodegradable calcium phosphate (CaP) coatings, faster osteointegration and bactericidal properties can be achieved. In this study, Cu-doped CaP supraparticles are spray-dried and suspension-sprayed CaP ceramic coatings with antibacterial properties are prepared using high-velocity suspension flame spraying (HVSFS). The objective was to increase the coatings’ porosity and investigate which Cu-doped supraparticles have the strongest antibacterial properties when introduced into the coating layers. Biocompatibility was tested on human Osteosarcoma cells MG63. A porosity of at least 13% was achieved and the supraparticles could be implemented, enhancing it up to 16%. The results showed that the addition of Cu-doped supraparticles did not significantly reduce the number of viable cells compared to the Cu-free sample, demonstrating good biocompatibility. The antimicrobial activity was assessed against the bacterial strains Escherichia coli and Staphylococcus aureus , with Safe Airborne Antibacterial testing showing a significant reduction in both Gram-positive and Gram-negative strains on the Cu-doped coatings.