Autor(en): | Häßner, Manuel Vinnik, Denis A. Niewa, Rainer |
Titel: | Thermal history dependent Al distribution in aluminum substituted strontium hexaferrite |
Erscheinungsdatum: | 2020 |
Dokumentart: | Zeitschriftenartikel |
Seiten: | 9 |
Erschienen in: | Materials 13 (2020), No. 858 |
URI: | http://nbn-resolving.de/urn:nbn:de:bsz:93-opus-ds-149789 http://elib.uni-stuttgart.de/handle/11682/14978 http://dx.doi.org/10.18419/opus-14959 |
ISSN: | 1996-1944 |
Zusammenfassung: | Single crystals of aluminum substituted strontium hexaferrite SrFe12-xAlxO19 were grown from sodium oxide based flux. The substitution level aimed for was x = 1.2. Annealing experiments performed on single crystals show that the Al distribution on the five iron sites of the hexaferrite structure depends on the annealing time at 900 °C. Single crystal X-ray diffractometry shows that annealing a crystal after the initial synthesis has an impact on the Al content on the octahedrally and tetrahedrally coordinated sites. Furthermore, it was found that heating in a corundum crucible increases the overall Al content. Magnetic measurements show that annealing in a platinum or corundum crucible decreases coercivity and remanence while the saturation magnetization is hardly influenced. |
Enthalten in den Sammlungen: | 03 Fakultät Chemie |
Dateien zu dieser Ressource:
Datei | Beschreibung | Größe | Format | |
---|---|---|---|---|
materials-13-00858-v2.pdf | 1,92 MB | Adobe PDF | Öffnen/Anzeigen |
Diese Ressource wurde unter folgender Copyright-Bestimmung veröffentlicht: Lizenz von Creative Commons