03 Fakultät Chemie
Permanent URI for this collectionhttps://elib.uni-stuttgart.de/handle/11682/4
Browse
3 results
Search Results
Item Open Access Chitin/cellulose blend fibers prepared by wet and dry‐wet spinning(2020) Ota, Antje; Beyer, Ronald; Hageroth, Ulrich; Müller, Alexandra; Tomasic, Patricija; Hermanutz, Frank; Buchmeiser, Michael R.We describe the wet and dry‐wet spinning of multifilament cellulosic composite fibers, namely chitin/cellulose fibers. The direct solution process for the two biopolymers based on an ionic liquid as solvent represents an environmentally friendly and alternative technology to the industrially applied viscose and lyocell process. Both cellulose and chitin possess good solubility in 1‐ethyl‐3‐methylimidazolium propionate ([C2C1Im][OPr]) and were spun into multifilament composite fibers. Moreover, for the first time, pure chitin multifilament fibers were obtained by dry‐wet spinning. The effect of chitin addition on the filament properties was investigated and evaluated by microscopic, spectroscopic, and mechanical analyses.Item Open Access High-performance cellulosic filament fibers prepared via dry-jet wet spinning from ionic liquids(2021) Vocht, Marc P.; Beyer, Ronald; Thomasic, Patricija; Müller, Alexandra; Ota, Antje; Hermanutz, Frank; Buchmeiser, Michael R.We report on a new process for the spinning of high-performance cellulosic fibers. For the first time, cellulose has been dissolved in the ionic liquid (IL) 1-ethyl-3-methylimidazolium octanoate ([C2C1im][Oc]) via a thin film evaporator in a continuous process. Compared to other ILs, [C2C1im][Oc] shows no signs of hydrolysis with water. For dope preparation the degree of polymerization of the pulp was adjusted by electron beam irradiation and determined by viscosimetry. In addition, the quality of the pulp was evaluated by means of alkali resistance. Endless filament fibers have been spun using dry-jet wet spinning and an extruder instead of a spinning pump, which significantly increases productivity. By this approach, more than 1000 m of continuous multifilament fibers have been spun. The novel approach allows for preparing cellulose fibers with high Young's modulus (33 GPa) and unprecedented high tensile strengths up to 45 cN/tex. The high performance of the obtained fibers provides a promising outlook for their application as replacement material for rayon-based tire cord fibers.Item Open Access Melt spinning of propylene carbonate‐plasticized poly(acrylonitrile)‐co‐poly(methyl acrylate)(2020) König, Simon; Kreis, Philipp; Reinders, Leonie; Beyer, Ronald; Wego, Andreas; Herbert, Christian; Steinmann, Mark; Frank, Erik; Buchmeiser, Michael R.The primary use of poly(acrylonitrile) (PAN) fibers, commonly referred to as acrylic fibers, is in textile applications like clothing, furniture, carpets, and awnings. All commercially available PAN fibers are processed by solution spinning; however, alternative, more cost‐effective processes like melt spinning are still highly desired. Here, the melt spinning of PAN‐co‐poly(methyl acrylate) (PMA) plasticized with propylene carbonate (PC) at 175°C is reported. The use of methyl acrylate (MA) as comonomer and PC as an external plasticizer renders the approach a combination of internal and external plasticization. Various mixtures of PAN and PC used in this work were examined by rheology, subjected to melt spinning, followed by discontinuous and continuous washing, respectively. The best fibers were derived from a PAN‐co‐PMA copolymer containing 8.1 mol‐% of MA having a number‐average molecular weight Mn of 34 000 g/mol, spun in the presence of 22.5 wt.‐% of PC. The resulting fibers were analyzed by scanning electron microscopy and wide‐angle X‐ray scattering (WAXS), and were subjected to mechanical testing.